UHMW PE Rail Pad for Concrete Sleeper - Assemblied with elastic rail fastening

UHMW PE rail pad for concrete sleeper:, 1. Insulation, 2. Low temperature resistant, 3. Wear resistant, 4. ISO9001 - details see: https://www.vehicleto.com/uhmw-pe-rail-pad-for-concrete-sleeper-10034487

Type: Tie Plates	Material: UHMW PE,Virgin UHMW PE	Dimensions (L x W x H) (mm): Customized	Place of Origin: Henan China (Mainland)
Brand Name: AYCG	Model Number: Assemblied with elastic rail fastening	Colour: Customized by customers	Special shape requirement: Available
Production technology: Extrusion or thermoforming

contact supplier for UHMW PE Rail Pad for Concrete Sleeper

Anyang Ultrahigh Industrial Technical Co., Ltd produces professionallyUHMW PE rail pad for concrete sleeper.

A. UHMW PE rail pad for concrete sleeper description

UHMWPEmaterial has exceptionally low coefficient of friction offering superb sliding properties and is one of the best plastics for wear/abrasion resistance meanwhile tough and impact resistant even at cryogenic temperatures. As a result, it is definite thatUHMW polyethyleneis a wonderful engineering plastic that can solve many problems that other engineering plastics cannot.

B. Characteristics for UHMW PE rail pad for concrete sleeper

1. UHMW exhibits virtually no water absorption

2, Non-Toxic

3. Low coefficient of friction

4. Corrosion resistant

5. Abrasion and impact resistant

6. Wear Resistant

7. Dielectric

8. Weatherproof

C. UHMWPE Application Areas

1. Textile Industry:

2. Chemical Industry:

3. Food Processing Industry:

4. Paper Industry:

5. Material Handling:

6. Farm Implement:

7. Mining & Metals Processing Industries:

8. Transportation:

9. Consumer Products:

10. Waste Water Treatment:

D. A parameter table for UHMWPE

Property	ASTM Test	Units Metric (US)	Typical Values
Specific Gravity	D792	gm/cm°	0.926-0.934
Tensile Strength @ Yield	D638	MPa (PSI)	21 (3100)
Tensile Strength @ Break	D638	MPa (PSI)	48 (7000)
Elongation @ Break	D638	%	350
Young's ("E") Modulus (23°C)	D638	MPa (PSI 10⁵)	690 (1.0)
Young's ("E") Modulus (-269°C)	D638	MPa (PSI 10⁵)	2970 (4.3)
Izod Impact Strength (23°C)	D256(1)	J/m (ft-LBS/in notch)	140 (30)
Izod Impact Strength (-40°C)	D256(1)	J/m (ft-LBS/in notch)	100 (21)
Hardness, Shore "D"	D2240	-	62-66
Abrasion Resistance	(2)	-	100
Water Absorption	D570	%	Nil
Relative Solution Viscosity	D4020	dl/gm	2.3-3.5
Density		(lbs./cubic in.)	.034